TECHNICAL SPECIFICATIONS FOR SEMI DULL PET CHIPS
ITEM		UNIT	INDEX
IV		DL/G	0.64±0.01
-COOH		MEQ/KG	≤30
MELTING POINT		°C	≥259
COLOR	L	-	≥80
	B	-	≤4.0
DEG		WT%	<0.2
ABNORMALLY CHIPS		WT%	≤0.3
TIO2 CONTENT		WT%	0.30±0.06
AGGLOMERATE PARTICLE(>=10UM)		AMOUNT/MG	≤1.0
POWDER		WT%	≤ 0.1

SUPER BRIGHT

TECHNICAL SPECIFICATIONS FOR SUPER BRIGHT PET CHIPS
ITEM		UNIT	INDEX
IV		DL/G	0.64± 0.01
-COOH		MEQ/KG	≤30
MELTING POINT		°C	≥259
COLOR	L	-	≤45
	B	---------- -	≤4.0
DEG		WT%	<0.2
ABNORMITY CHIPS		WT%	≤0.3
H2O CONTENT		WT%	<0.2
AGGLOMERATE PARTICLE(>=10UM)		AMOUNT/MG	≤1.0
POWDER		WT%	≤0.1
Ti02		WT %	0.00%

CATIONIC DYED

TECHNICAL SPECIFICATION OF CATIONIC DYED CHIPS
NO	ITEM	UNIT	FILAMENT GRADE
1	RELATIVE VISCOSITY MEASURED IN 1% (W/W) POLYESTER M CRESOL SOLUTION IV RELATIVE VISCOSITY	%	1.540±0.025 AT 20+/-0.02 ° C 0.535± 0.025
2	TiO2 CONTENT 720 °C OVEN /UV INSTRUMENT	%	0.10± 0.02%
3	ACID VALUE PHENOL / CHLOROFORM -1:1 MANU TITRATION KOH / BENZYL ALCOHOL	µeq / gr	MAX50
4	WHITENESS NIPPON DP-1001 INSTRUMENT LUMINANCE -L YELLOWNESS-B	%	69.0±5.0 MAX 4.0
5	DEG CONTENT KOH / N-PROPYL ALCOHOL GC INSTRUMENT	%	MAX 4.0
6	MELTING POINT DSC INSTRUMENT	°C	246.0±3
7	WATER CONTENT OVEN 105 DEGREE C	%	MAX 0.5%
8	ASH CONTENT OVEN 720 DEGREE C
9	CHIPS DIMENSION VERNIER CALIPER MEASURING	M/M	2.5 ø* 3.3 ø* 3.3ø ±0.3

FILM GRADE

TECHNICAL SPECIFICATIONS FOR FILM GRADE CHIPS
ITEM		UNIT	INDEX
IV		DL/G	0.64± 0.01
-COOH		MEQ/KG	≤30
MELTING POINT		°C	≥259
COLOR	L	-	≤45
	B	------------ -	≤4.0
DEG		WT%	<0.2
ABNORMITY CHIPS		WT%	≤0.3
H2O CONTENT		WT%	<0.2
AGGLOMERATE PARTICLE(>=10UM)		AMOUNT/MG	≤1.0
POWDER		WT%	≤0.1
Ti02		WT %	0.00%

MASTER BATCH

THE CARBON BLACK (C.I NAME ) USED CONTAINS POLYCYCLIC AROMATIC HYDROCARBON LESS THAN 01% WHICH IS THE SPECIFIED LIMIT. THE CARBON BLACK USED IS NON TOXIC, ECO FRIENDLY AND NON CARCINOGENIC. THE MASTER BATCH DOES NOT HAVE ANY ORANGE 37/36 COLORANT IN IT. NO PRODUCT INSIDE THE CARBON THAT CAN INCREASE THE RISK OF CARCINOGENIC EFFECT INGREDIENTS ARE FOOD GRADE AND ACCORDING TO THE DATA SHEET.

TECHNICAL SPECIFICATION 0F MASTER BATCH
SPECIFICATIONS	DETAILS
CARRIER RESIN	PBT
COMPATIBILITY WITH PET	EXCELLENT
CARBON BLACK LOADING	30%
TONE	JET BLACK BLUISH TONE
IV FOR BASE POLYMER	0.82
FILTER INDEX	LESS THAN 0.2 MPA/KG
SPINNABILITY	VERY GOOD
HEAT STABILITY	MORE THAN 300 ° C
LIGHT FASTNESS	8
MOISTURE CONTENT	LESS THAN 0.8%
SHELF LIFE	MORE THAN 18 MONTHS
MELTING POINT	225 °C TO 228° C
REQUIRED LDR	3.8 FOR 150 D
IV(UNCORRECTED)	0.52 TO 0.56

FIRE RETARDANT SEMI DULL CHIPS

The permanent flame retardant polyester chips (PET), is made from phosphorous co-polymerizing FR, PTA and EG through their copolycondensation reaction, in order flame retardant monomer to be inserted or linked to molecular chain of polyester.

No.	Item	Unit	A + grade	A grade	B grade
1	Intrinsic viscosity	d1/g	0.02	0.025	0.03
2	Melt point	¡æ	240	235	230
3	Carboxy1 end group content	mol/t	40	45	45
4	Chromatic value (b)		8	8	8
5	DEG	wt%	3.0	3.5	3.5
6	Titanium dioxide content	%	0.05	0.05	0.05
7	Agglomeration particle	¸ö/mol	1.0	3.0	6.0
8	Moisture	%	0.3	0.4	0.5
9	Ash content	%	0.4	0.5	0.6
10	Iron	mg/kg	8	10	12
11	Limiting oxygen index	%	29	29	28

BOTTLE GRADE CHIPS

hot filled bottles

SPECIFICATIONS FOR HOT FILLED BOTTLE GRADE PET
ITEM		UNIT	INDEX
I.V		DL/G	0.78±0.02
CRYSTALLINITY		%	<60
COLOR VALUE	L	-	≥83
	B	-	≤1.0
CONTENT OF ACETALDEHYDE		PPM	≤1.0
MELTING POINT		°C	249±2
WT OF 20 CHIPS		G	0.34±0.01

oil bottles

SPECIFICATION FOR OIL BOTTLES GRADE PET
ITEM		UNIT	INDEX
I.V		DL/g	0.83±0.02
CRYSTALLINITY		%	<60
COLOR VALUE	L	-	≥83
	B	-	≤1.0
CONTENT OF ACETALDEHYDE		PPM	≤1.0
DUST CONTENT		PPM	≤100
MELTING POINT		*C	≤248
WT OF 20 CHIPS		G	0.34±0.01

carbonated soft drink

SPECIFICATIONS FOR CSD BOTTLE GRADE PET
ITEM		UNIT	INDEX
I.V		DL/G	0.85±0.02
CRYSTALLINITY		%	<60
COLOR VALUE	L	-	>=83
	B	-	≤1.0
CONTENT OF ACETALDEHYDE		PPM	≤1.0
DUST CONTENT		PPM	≤100
MELTING POINT		*C	≤245
WT OF 20 CHIPS		G	0.34±0.01

distilled water bottles

TECHNICAL SPECIFICATION 0F PURE WATER BOTTLE GRADE POLYESTER CHIPS
PROPERTY		UNIT	VALUE
I.V.		Dl/G	0.80±0.02
WATER CONTENT		Wt%	<0.5
MELTING POINT		ºC	≤248
COLOR VALUE	L	-	≥82
	B	-	≤1.0
CRYSTALLINITY		%	<60
CHIP SHAPE		SPINNABILITY	ELLIPTICAL CYLINDER
WEIGHT OF 100CHIPS		G	1.70±0.10
PACKING		Kg/Bag	1050
A.A CONTENT		PPM	≤1.0
DUST CONTENT		PPM	≤100
MOLDING TEMP		ºC	265-270

NYLON CHIPS SEMI DULL

Technical Specifications of Nylon 6 chips semi dull
TEST DESCRIPTION	SET VALUE	ANALYSIS
RELATIVE VISCOSITY	2.48±0.03	2.472
NH2 10`6 mol/G	44±3	44.56
H2O PPM	<-800	376
TiO2%	0.29±0.05	0.28
EXTRACTABLE%	<0.6	0.33
CHIP SIZE	Mm	2.5*2.5